FIBERGLASS BOATBUILDING: Resins and Laminating Techniques

A barrel of polyester resin

In the last installment of our continuing exploration of how fiberglass sailboats get built we looked at the different types of fabric that can be used to create a laminate. As mentioned in our first episode, however, any fiberglass laminate is in fact a composite material (just like papier-mâché), consisting both of glass fabric, which provides structural strength, and plastic resin, which serves as the binding agent that allows the otherwise floppy fabric to maintain a fixed molded shape. The resin, not surprisingly, is just as important as the fabric in determining the qualities of any laminate.

The cheapest, most common types of resin are polyester. These were used exclusively in the early days of fiberglass boatbuilding and are still the most popular today. Polyester resin begins to harden the moment it is created; to stop this and keep the resin in a liquid state, an inhibitor must be added. The function of the catalyst (usually methyl ethyl ketone and peroxide, or MEKP) is to destroy the inhibitor and reinitiate the curing process. The inhibitor breaks down eventually anyway, which means polyester resin has a limited shelf life. Polyester resin also will not cure at room temperature unless an accelerator (usually purple cobalt naphthenate) is added to it. Normally this is added when the resin is manufactured; otherwise it must be added separately, or the resin must be cured in an oven.

Common polyester resins are based on either orthophthalic or isophthalic acids. Ortho-polyester resins are the weakest and most brittle of all resins used in boatbuilding. If used with unidirectional or multiaxial glass fabrics, or more exotic fabrics like Kevlar or carbon fiber, they will crack before the fabric’s full strength is utilized. They are also the most vulnerable to chemical attack and are the least water resistant. This last feature is particularly important, as the more easily water can pass through a resin into a laminate, the more likely it is the laminate will develop osmotic blisters over time.

Iso-polyester resins are slightly less brittle and are considerably more chemical and water resistant. They are also, of course, more expensive. Builders therefore commonly use iso-polyesters in the gelcoat and external layers of a laminate and cheaper ortho-polyesters in the internal layers. Iso-polyester resins are just strong enough to support most sophisticated glass fabrics, though they are probably not quite strong enough to be used effectively with exotic fabrics.

Vinylester resins are the next step up in quality and cost. They are similar to polyester resins and utilize the same catalysts, but are markedly stronger. For example, a good iso-polyester resin may elongate by as much as 2.5 percent along its length before failing and fracturing and has a tensile strength of about 9,400 pounds per square inch. A vinylester resin, by comparison, can elongate up to 5 percent of its length before fracturing and has a tensile strength of about 11,800 pounds per square inch. This makes vinylester the resin of choice when laminating with more sophisticated fabrics. Vinylester is also much more water resistant than both ortho- and iso-polyester resins, thus is less prone to blistering.

Because they are chemically similar and bond to each other well in both a cured and uncured state, vinylester and polyester can be used interchangeably in a laminate. This gives builders great flexibility. As boat buyers have become ever more wary of blisters, even mass-production builders now increasingly use vinylester resin in the exterior layers of a laminate to reduce water permeability. They then switch to polyester to finish the bulk of the laminate and so keep costs under control. Vinylester is now also commonly used throughout laminates in racing and high-quality cruising boats.

The best, most expensive boatbuilding resin is epoxy, which is stronger than both polyester and vinylester. Its elongation before failure is usually more than 5 percent, and its tensile strength is about 12,500 pounds per square inch. Epoxy is also more adhesive, forms better bonds (particularly post-cure bonds), and is even more water resistant (and thus more blister resistant) than vinylester resin.

West System epoxy resin

Epoxy resin, however, is fundamentally different from polyester and vinylester resins. Its secondary component is not a catalyst that enables a chemical reaction, but a hardener that is integral to the reaction that causes epoxy to set and solidify. To achieve full structural strength, it is best to post-cure epoxy at elevated temperatures. It is incompatible with most chopped-strand mat, as it does not properly dissolve the binder in the fabric. Plus, it is only semi-compatible with vinylester and polyester; it may be laid down on top of cured polyester and vinylester, but they may not be laid down on it, whether it has cured or not.

Epoxy is often used when making repairs to fiberglass boats and may be used in the secondary phase of construction when structural parts are being attached to an already cured hull. Epoxy is also often applied below the waterline as a barrier coat to prevent blistering. But because it is so very expensive, it is rarely used as the primary resin in a laminate, except in the most cutting-edge boats.

 

Laminating techniques

The easiest way to lay up a fiberglass hull is by hand in an open mold. The resin itself can be applied in different ways. The crudest method is to simply slap it on with brushes from buckets of catalyzed resin. Now, however, it is more common to see workers wetting out fabric with airless spray guns or special resin-fed rollers. With spray guns the resin and catalyst are mixed as they are sprayed onto the fabric. With rollers the resin is catalyzed just before being pumped to the roller head.

Spray guns and rollers obviate the need to constantly mix small batches of resin, which remains perfectly fluid for only a few minutes after it is catalyzed. Though it takes a long time to cure completely (unless post-cured at higher than room temperatures), resin only remains “wet” in any meaningful sense for a few hours. This is important because for one layer of a laminate to form a chemical bond and cross-link with another on a molecular level they must be laid on each other “wet on wet.” If the receiving layer is too dry, the bond with the next layer is only adhesive and is not nearly as strong.

Each step in creating an open-mold laminate is therefore a race to get the next layer of fabric laid down and wet out before the previous one sets up too hard. One advantage of using polyester and vinylester resins is that the time it takes for the resin to kick can be controlled by using varying amounts of catalyst. But this only buys so much time. The maximum recommended time between the application of layers is normally about 16 hours, but the shorter the interval the better. This is less daunting when working on a small hull, but if the hull is large it can be problematic. In many cases, ideal chemical bonds are not always achieved and some areas of an open-mold laminate end up inherently weaker than others.

Voids are another problem. These are small pockets of air that get trapped in a laminate as it is laid up. They not only undermine the laminate’s solidity, they also promote blistering by providing places for moisture in the laminate to pool up and mix with chemicals in the resin.

The simplest way to drive air out of a laminate so it sets up solid is to compress the layers of wet-out fabric together with handheld rollers. These rollers have ribs that help crush air bubbles and spread resin more evenly through the fabric. This increases the fabric-to-resin ratio, thus increasing the laminate’s strength relative to its weight. Using rollers, however, is labor intensive, and the extra time spent squishing down each layer of wet fabric only decreases the chances of a chemical bond being formed with the next layer.

Laminating fiberglass by hand

There is a more sophisticated technique for pressing air out of a laminate, called vacuum bagging, that has been around since the earliest days of fiberglass boat building. Here a plastic skin is taped over a layer of laminate after it is laid down and wet out, then air is pumped out from beneath the plastic. The vacuum applies a large amount of pressure evenly over the entire surface of the laminate; the end result is a denser, more void-free layup than can be achieved working by hand.

An even better technique for both saturating fabric with resin and squeezing everything together involves a process known generically as resin infusion. There are numerous variations, but the best known is a proprietary procedure called the Seemann Composites Resin Infusion Molding Process, or SCRIMP. Here all the laminate layers are laid down together dry in a mold and are tacked in place with spray adhesive. The entire dry laminate is then covered with a plastic vacuum bag plumbed with a network of tubes connected to vats of resin. Air is pumped out of the bag and resin is sucked through the tubes into the laminate. Once the laminate is fully saturated, the flow of resin is shut off and the laminate is then allowed to set up under pressure.

Preparing a hull for resin infusion

There are several advantages to this. The laminate layers are sure to form chemical bonds with one another, because they are saturated simultaneously. Only the minimum amount of resin needed to wet out the fabric is used, so the laminate’s fabric-to-resin and strength-to-weight ratios are optimal. Finally, as with straight vacuum bagging, the resulting laminate is dense with minimal voids.

Resin infusion is also a much cleaner process. Both polyester and vinylester resins contain significant amounts of styrene, the vapors of which are classified as a hazardous air pollutant by the U.S. Environmental Protection Agency. It is styrene that gives fresh fiberglass its strong sweet chemical odor and makes it necessary for workers handling resin to wear protective clothing and respirators.

Unlike open-mold layups, where the resin fumes all escape into the atmosphere, resin infusion allows for emissions containment. As boatbuilders come under increasing regulatory pressure to limit styrene emissions, they will likely be forced to abandon open-mold building methods and rely exclusively on resin infusion instead. This inevitably will drive up the cost of fiberglass boat production and may force some builders out of business. It may instead be possible to use new low-styrene resins, but so far these set up too quickly to allow chemical bonds to form between layers in a laminate.

The challenge of resin infusion, other than the extra expense, is that it must be done very carefully. Any tiny leaks in the vacuum bag or resin tubes leads to air getting sucked into the laminate. The distribution of resin through the laminate must also be carefully monitored. If resin is unevenly distributed or is cut off prematurely, the result can be a resin-starved laminate with patches of dry fabric buried within it. Builders must play a fine game here--if they use too much resin, a boat will be heavier (and weaker) than necessary; if they use too little, it may delaminate in short order. In recent years there have been some dramatic failures of this sort where large expensive boats with resin-infused hulls have required extensive post-production repairs.

Quality control is important no matter how a hull is laminated. Resin can be significantly degraded if not stored and handled properly. Shelf life must be closely monitored, drums must be kept carefully sealed in a dark climate-controlled environment, the resin itself must be carefully stirred before being removed from a drum, and must also be carefully mixed with proper amounts of catalyst. Climate, too, must be closely monitored. If a workspace is too hot, too cold, or too humid, the quality of a laminate can be seriously compromised.

Unfortunately, there is no way a boat buyer can be sure that a builder has produced a sound laminate. Buyers of new high-end fiberglass boats with resin-infused hulls now sometimes insist on clear gelcoat so they can visually inspect for voids and resin-starvation prior to painting the hull. Surveyors routinely inspect hulls by sounding them with hammers, listening for dead spots that indicate lamination problems; they also scan hulls with moisture meters to find water-saturated areas. Such precautions are helpful, but certain issues--such as poor climate control, poor bonding within a laminate, mishandling of resins and/or catalysts, etc.--may never come to light until a laminate actually fails.

The most common problem owners have with hull laminates is blistering. We'll explore this in more detail in our next installment!

 

Search

Total Cruise Control

Buy Total Cruise Control On Amazon Click Here

Buy Total Cruise Control On Amazon Click Here